Max service temperature:1250 SiO2: ≧ 98% Al2O3: ≦1% Fe2O3: ≦0.2% Bulk Density: ≧1.75g/cm3 Cold Crushing Strength: ≧35MPa Thermal Shock resistance ,cycles (1100℃ to cool water): ≧50 Refractoriness under load (0.2Mpa.0.6%): ≧1650 Thermal expansion coefficient (Room Temp to 1000℃): 0.6 Fused silica brick is a kind of high-precision and high-purity quartz material. It is also called fused quartz brick or Zero Expansion Silica Brick. The production method is to melt pure quartz sand made by melting pure quartz sand in an electric furnace and heating to more than 1800 ° C, and then cut through professional cutting equipment. Different sizes of fused silica bricks can be produced. Ordinary purity SiO2> 99.5%. High purity SiO2≥99.99%. As a professional fused silica bricks manufacturer, we have exported different fused silica refractory materials to more than 30 countries. Please kindly read the following more information and make Inquiry.

Scope of application

• Fused silica brick mainly used to build the upper pool wall of the furnace used for melting low alkali borosilicate glass. It's an ideal refractory brick for glass furnace hot repair

Advantage

• Tiny thermal expansion coefficient • Good thermal shock resistance • High purity, corrosion resistant • High viscosity at high temperature, high strength • Strong slag resistance and strong impact resistance • Low thermal conductivity • No Firing shrinkage.

Item	Fused silica brick	Fused silica saggar	Clay bonded fused silica brick
Max service temperature	1250	1250	1250
SiO2% ≧	98	98	95
Al2O3% ≦	1	1	4
Fe2O3% ≦	0.2	0.2	0.2
Bulk Density（g/cm3）≧	1.75	1.7	1.75
Cold Crushing Strength(MPa)≧	35	30	30
Thermal Shock resistance ,cycles (1100℃ to cool water)≧	50	50	40
Refractoriness under load (0.2Mpa.0.6%)≧	1650	1600	-
Thermal expansion coefficient (Room Temp to 1000℃)	0.6	0.6	0.8