Main Composition:MgO Application:Various kinds of industrial kiln Capacity:1000 tons per month Color:Yellow Size:As your requirements

Product Introduction

Magnesia bricks are alkali-resistant materials with good fire resistance and corrosion resistance, and strong resistance to alkali slag. The refractoriness of magnesia brick is above 2000℃. Magnesia bricks are widely used in inspection rooms of glass jars, lime kilns, non-ferrous metallurgical furnaces, open-air furnaces, iron stirrers and electric arc furnaces.

Features

1.High refractoriness, usually refractoriness above 2000℃. 2. High refractoriness under load. 3. Excellent slag wear resistance and higher bulk density. 4. Lower apparent porosity and lower impurity content.

Application

Magnesia Brick is mainly used for furnace lining, furnace bottom and furnace wall, oxygen converter permanent lining, non-ferrous metal smelting furnace, high temperature tunnel kiln, calcined magnesia and cement rotary kiln lining, furnace bottom and furnace wall, glass furnace regenerative lattice Bricks, etc.

Item		MD92	MD95	MD97	MD98
Composition(%)	MgO	92	95	97	97.5
	CaO	2.5	2.0	1.6	1.2
	SiO2	3.5	2.5	1.2	0.6
Bulk Density(g/cm3)		2.90	2.95	3.00	3.00
Refractoriness Under Load T2 (ºC)		1550	1650	1700	1700
Apparent Porosity (%)		18	16	15	15
Cold Crushing Strength(MPa)		55	60	70	80
Thermal Shock Resistance 950ºC  air cool (times)		10	10	10	10