Good Raw Material Strict Quality Control Strict Lab Test Fast Delivery Time 100% Factory Price Credit Assurance Satifisfied Service Silicon carbide brick is a refractory material made of SiC as the main raw material. The silicon carbide content is from 72% to 99%. Mohs hardness 9. Generally, black silicon carbide (SiC content above 96%) is used as the raw material, and the binder (or no binder) is added, and then it is prepared by batching, mixing, molding and firing. The main crystal phase is silicon carbide. Silicon carbide refractory brick is mainly divided into several types of clay bonding, Si3N4 bonding, Sialon bonding, β-SiC bonding, Si2ON2 bonding and recrystallization. It is stable to acidic slag and has good wear resistance, corrosion resistance, high temperature strength, good thermal shock stability, high thermal conductivity, and low thermal expansion coefficient. It is a high-performance refractory material. As a professional silicon carbide bricks manufacturer, we have exported different silicon carbide refractory bricks to more than 30 countries. Please kindly read the following more information and make Inquiry

Scope of application:

The main purpose of silicon carbide bricks is to serve as the lining of thermal equipment. According to the parts of the thermal equipment, different combinations can be used to produce silicon carbide products of different specifications, such as silicon carbide plates, silicon carbide rings and etc. In the metallurgical industry, silicon carbide bricks are mainly used in aluminum melting furnaces for aluminum alloy smelting, secondary tuyere bricks of blast furnaces and etc.; In the power industry, they are mainly used in boilers as the nozzle of the boiler combustion chamber; in the domestic garbage treatment industry, the bricks are used in waste incinerators.

Advantage:

• Good wear resistance and corrosion resistance • Good strength at high temperature • Good thermal shock stability • High thermal conductivity • Low thermal expansion coefficient

Items	Oxide bonded SIC brick	Corundum-SIC brick	Mullite-SIC brick	Alumina-SIC brick	Si3N4-SIC brick
SiC  %	≥85	≥70	≥65	≥20	≥72
Al2O3  %	---	≥20	≥20	≥55	---
Si3N4  %	---	---	---	---	≥19
Bulk density (g/cm3)	≥2.5	≥2.6	≥2.3	≥2.5	≥2.65-2.7
Apparent porosity %	≤18	≤20	≤20	≤22	≤14-18
Cold compression strength (Mpa)	≥100	≥100	≥80	≥80	≥200
Refractoriness under load (0.2Mpa,0.6%)	≥1700	≥1700	≥1650	≥1550	≥1600
Thermal Conductivity W/(m.k) 1200℃	13.2	9-10	12	6-8	16
Thermal shock resistance Water quenching at 1100℃ (time)	≥40	≥30	≥40	≥30	≥30